Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Material materials with Dichte of 1.19 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 1.87 GPa Show Material materials with Biegemodul of 1.87 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 150 % Show Material materials with Dehnung of 150 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527 | 50 mm/min |
Flexural yield strength | 23.0 °C | 72 MPa Show Material materials with Flexural yield strength of 72 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 |
23.0 °C | 800 J/m Show Material materials with Impact strength, Izod notched, ASTM of 800 J/m | ASTM D 256 | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 44 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 44 kJ/m² | ISO 180/1A |
23.0 °C | 52 - 54 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 52 - 54 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 54 MPa Show Material materials with Streckgrenze of 54 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 45 MPa Show Material materials with Zugfestigkeit of 45 MPa | ISO 527 | 50 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 90 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 6 cm³/10min Show Material materials with Schmelzvolumenflussrate of 6 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.8 - 1 % Show Material materials with Schrumpfung of 0.8 - 1 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.8 - 1 % Show Material materials with Schrumpfung, diagonal of 0.8 - 1 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Circuit Protection,City,Door Handle,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,Exterior Rail Components,Exterior Trim,Heavy Vehicles,Individual Equiptment,LED Lighting,Motorcycle,Non-LED Lighting,Personal Care,Personal Water Craft,Recreational Vehicle,Refrigerator,Vacuum Cleaner | |
Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm |