Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.2 g/cm³ Show Material materials with Dichte of 1.2 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 74 MPa Show Material materials with Biegefestigkeit of 74 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 2.01 GPa Show Material materials with Biegemodul of 2.01 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 110 % Show Material materials with Dehnung of 110 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 1.98 GPa Show Material materials with Elastizitätsmodul of 1.98 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 4.1 % Show Material materials with Elongation at yield of 4.1 % | ASTM D 638 | Type I, 5 mm/min |
Flexural strain | 23.0 °C | 7.3 % Show Material materials with Flexural strain of 7.3 % | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 78 MPa Show Material materials with Flexural yield strength of 78 MPa | ISO 178 | 2 mm/min |
Härte, Shore D | 23.0 °C | 79 [-] Show Material materials with Härte, Shore D of 79 [-] | ISO 868 |
Impact strength, Izod notched, ASTM | -40.0 °C | 372 J/m Show Material materials with Impact strength, Izod notched, ASTM of 372 J/m | ASTM D 256 |
-30.0 °C | 489 J/m Show Material materials with Impact strength, Izod notched, ASTM of 489 J/m | ASTM D 256 | |
-20.0 °C | 687 J/m Show Material materials with Impact strength, Izod notched, ASTM of 687 J/m | ASTM D 256 | |
-10.0 °C | 695 J/m Show Material materials with Impact strength, Izod notched, ASTM of 695 J/m | ASTM D 256 | |
23.0 °C | 755 J/m Show Material materials with Impact strength, Izod notched, ASTM of 755 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 47 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 47 kJ/m² | ISO 179/1eA |
23.0 °C | 62 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 62 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -40.0 °C | 34 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 34 kJ/m² | ISO 180/1A |
-30.0 °C | 51 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 51 kJ/m² | ISO 180/1A | |
23.0 °C | 63 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 63 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 45 MPa Show Material materials with Streckgrenze of 45 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 46 MPa Show Material materials with Zugfestigkeit of 46 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 16 g/10min Show Material materials with Schmelzmassenflussrate of 16 g/10min | ISO 1133 | 250°C/5 kg | |
Schrumpfung | 23.0 °C | 0.8 - 1 % Show Material materials with Schrumpfung of 0.8 - 1 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.8 - 1 % Show Material materials with Schrumpfung, diagonal of 0.8 - 1 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Spoiler | |
| Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm | |