Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 0.96 g/cm³ Show Material materials with Dichte of 0.96 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 1.31 GPa Show Material materials with Biegemodul of 1.31 GPa | ISO 178 | 2 mm/min, 64mm |
Dehnung | 23.0 °C | 59.7 % Show Material materials with Dehnung of 59.7 % | ISO 527 | 50 mm/min |
Elastizitätsmodul | 23.0 °C | 1.31 GPa Show Material materials with Elastizitätsmodul of 1.31 GPa | ISO 527 | 1 mm/min |
Elongation at yield | 23.0 °C | 5.4 % Show Material materials with Elongation at yield of 5.4 % | ISO 527 | 50 mm/min |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 3 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | ISO 179/1eA |
23.0 °C | 17 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 17 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 3 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 3 kJ/m² | ISO 180/1A |
23.0 °C | 26 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 26 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 21 MPa Show Material materials with Streckgrenze of 21 MPa | ISO 527 | 50 mm/min |
Zugfestigkeit | 23.0 °C | 14 MPa Show Material materials with Zugfestigkeit of 14 MPa | ISO 527 | 50 mm/min, 1A |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 55 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 55 °C | ISO 75-1&2 | 1.8 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9.9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 9.9E-5 1/K | ISO 11359-2 | -30°C to 100°C |
Vicat-Erweichungstemperatur | 133 °C Show Material materials with Vicat-Erweichungstemperatur of 133 °C | ISO 306 | 10N, 50°C/hr | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.62E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.62E-4 1/K | ISO 11359-2 | -30°C to 100°C |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Schmelzmassenflussrate | 19 g/10min Show Material materials with Schmelzmassenflussrate of 19 g/10min | ISO 1133 | 230°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Exterior application | |
| Fillers | Mineral Powder | |
| Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa | |