Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.17 g/cm³ Show Material materials with Dichte of 1.17 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.13 % Show Material materials with Wasserabsorption of 0.13 % | ASTM D 570 | 24 Hours |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 1.72 GPa Show Material materials with Biegemodul of 1.72 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 165 % Show Material materials with Dehnung of 165 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 68 MPa Show Material materials with Flexural yield strength of 68 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -40.0 °C | 534 J/m Show Material materials with Impact strength, Izod notched, ASTM of 534 J/m | ASTM D 256 |
23.0 °C | 801 J/m Show Material materials with Impact strength, Izod notched, ASTM of 801 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 3204 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 |
Streckgrenze | 23.0 °C | 49 MPa Show Material materials with Streckgrenze of 49 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 96 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 96 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating | 1.49mm | UL 94 | ||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.95 [-] Show Material materials with Dielektrizitätskonstante of 2.95 [-] | ASTM D 150 | at 1 MHz |
Durchschlagfestigkeit | 23.0 °C | 19.8 kV/mm Show Material materials with Durchschlagfestigkeit of 19.8 kV/mm | ASTM D 149 | in air, 3.2 mm |
Verlustfaktor | 23.0 °C | 0.03 [-] Show Material materials with Verlustfaktor of 0.03 [-] | ASTM D 150 | at 1 MHz |
spezifischer Widerstand | 23.0 °C | 9.50E+14 Ω·m Show Material materials with spezifischer Widerstand of 9.50E+14 Ω·m | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schrumpfung | 23.0 °C | 1 - 1.2 % Show Material materials with Schrumpfung of 1 - 1.2 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Amusement Machine,ATM/Ticket Machine,Audio,Data Transfer,Document Handling,Electronic Components,Enclosure/Housing/Cover,Industrial Material Handling,Lab Ware and Clinical Diagnostics,Medical Device,Personal Computing,Photovoltaic Components,Security/Detection | |
| Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm | |