Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.16 g/cm³ Show Material materials with Dichte of 1.16 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 4.1 GPa Show Material materials with Biegemodul of 4.1 GPa | ISO 178 | 2 mm/min, 64mm |
Dehnung | 23.0 °C | 4 % Show Material materials with Dehnung of 4 % | ISO 527 | 50 mm/min |
Elastizitätsmodul | 23.0 °C | 4.75 GPa Show Material materials with Elastizitätsmodul of 4.75 GPa | ISO 527 | 1 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ISO 527 | 50 mm/min |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 1 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 1 kJ/m² | ISO 179/1eA |
23.0 °C | 1 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 1 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 1 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 1 kJ/m² | ISO 180/1A |
23.0 °C | 1 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 1 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 34 MPa Show Material materials with Streckgrenze of 34 MPa | ISO 527 | 50 mm/min |
Zugfestigkeit | 23.0 °C | 33 MPa Show Material materials with Zugfestigkeit of 33 MPa | ISO 527 | 50 mm/min, 1A |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75-1&2 | 1.8 MPa | |
Koeffizient der thermischen Ausdehnung | -30.0 °C | 5.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 5.8E-5 1/K | ISO 11359-2 |
Vicat-Erweichungstemperatur | 157 °C Show Material materials with Vicat-Erweichungstemperatur of 157 °C | ISO 306 | 10N, 50°C/hr | |
thermischer Ausdehnungskoeffizient, transversal | -30.0 °C | 1.25E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.25E-4 1/K | ISO 11359-2 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 16 g/10min Show Material materials with Schmelzmassenflussrate of 16 g/10min | ISO 1133 | 230°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.75 % Show Material materials with Schrumpfung of 0.75 % | SABIC method | 48 hrs @ 23°C |
Schrumpfung, diagonal | 23.0 °C | 1.25 % Show Material materials with Schrumpfung, diagonal of 1.25 % | SABIC method | 48 hrs @ 23°C |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Under the hood | |
| Fillers | Talc | |
| Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa | |