| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.31 g/cm³ Show Material materials with Dichte of 1.31 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.08 % Show Material materials with Wasserabsorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.4 GPa Show Material materials with Biegemodul of 2.4 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 15 % Show Material materials with Dehnung of 15 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.5 GPa Show Material materials with Elastizitätsmodul of 2.5 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 85 MPa Show Material materials with Flexural yield strength of 85 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 145 MPa Show Material materials with Hardness, Ball Indentation of 145 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Material materials with Hardness, Rockwell R of 117 [-] | ISO 2039-2 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 36 J/m Show Material materials with Impact strength, Izod notched, ASTM of 36 J/m | ASTM D 256 | ||
23.0 °C | 38 J/m Show Material materials with Impact strength, Izod notched, ASTM of 38 J/m | ASTM D 256 | |||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/2C | ||
23.0 °C | 4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/2C | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 4 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A | ||
23.0 °C | 4 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A | |||
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 100 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 100 kJ/m² | ISO 180/1U | ||
Streckgrenze | 23.0 °C | 60 MPa Show Material materials with Streckgrenze of 60 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 60 MPa Show Material materials with Zugfestigkeit of 60 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ 23,-30°C | ASTM D 4812 | ||||
Schlagzähigkeit, Charpy ungekerbt | No break @ 23°C | ISO 179/2C | ||||
Thermisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 260.0 °C | 165 Pa·s Show Material materials with Melt viscosity of 165 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzvolumenflussrate | 50 cm³/10min Show Material materials with Schmelzvolumenflussrate of 50 cm³/10min | ISO 1133 | 250°C/5.0 kg | |
Schrumpfung | 23.0 °C | 1.3 - 2 % Show Material materials with Schrumpfung of 1.3 - 2 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 1.1 - 2 % Show Material materials with Schrumpfung, diagonal of 1.1 - 2 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Coffee Maker/Espresso Machine,Dishwasher,EV Infrastructure,Food Container,Hygiene/Personal Care,Water Treatment/Filtration,Wireless Communications | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |