| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.26 g/cm³ Show Material materials with Dichte of 1.26 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.13 % Show Material materials with Wasserabsorption of 0.13 % | ISO 62 | 23°C, 50% RH |
Wasseraufnahme, Gleichgewicht | 23.0 °C | 0.31 % Show Material materials with Wasseraufnahme, Gleichgewicht of 0.31 % | ASTM D 570 |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 108 MPa Show Material materials with Biegefestigkeit of 108 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Biegemodul | 23.0 °C | 3.4 GPa Show Material materials with Biegemodul of 3.4 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 12 % Show Material materials with Dehnung of 12 % | ASTM D 638 | Type I, 5 mm/min | ||
Elastizitätsmodul | 23.0 °C | 3.93 GPa Show Material materials with Elastizitätsmodul of 3.93 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural yield strength | 23.0 °C | 95 MPa Show Material materials with Flexural yield strength of 95 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 115 MPa Show Material materials with Hardness, Ball Indentation of 115 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 124 [-] Show Material materials with Hardness, Rockwell R of 124 [-] | ASTM D 785 | ||
Härte, Rockwell M | 23.0 °C | 85 [-] Show Material materials with Härte, Rockwell M of 85 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 80 J/m Show Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 | ||
23.0 °C | 107 J/m Show Material materials with Impact strength, Izod notched, ASTM of 107 J/m | ASTM D 256 | |||
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1602 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 1602 J/m | ASTM D 4812 | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 15 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/2C | ||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | ||
23.0 °C | 8 - 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 - 10 kJ/m² | ISO 180/1A | |||
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 130 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 130 kJ/m² | ISO 180/1U | ||
Streckgrenze | 23.0 °C | 63 MPa Show Material materials with Streckgrenze of 63 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Zugfestigkeit | 23.0 °C | 48 MPa Show Material materials with Zugfestigkeit of 48 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 138 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 138 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.68E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 4.68E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Spezifische Wärmekapazität | 23.0 °C | 1210 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 1210 J/(kg·K) | ASTM C 351 | ||
Vicat-Erweichungstemperatur | 149 °C Show Material materials with Vicat-Erweichungstemperatur of 149 °C | ASTM D 1525 | Rate B/50 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.21 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.21 W/(m·K) | ISO 8302 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.46E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.46E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94-5VB Rating | 2mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.9 [-] Show Material materials with Dielektrizitätskonstante of 2.9 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 16 kV/mm Show Material materials with Durchschlagfestigkeit of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Kriechstromfestigkeit | 23.0 °C | 175 V Show Material materials with Kriechstromfestigkeit of 175 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Material materials with Verlustfaktor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 7 g/10min Show Material materials with Schmelzmassenflussrate of 7 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schmelzvolumenflussrate | 7 cm³/10min Show Material materials with Schmelzvolumenflussrate of 7 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Circuit Protection,Data Transfer,Displays,Document Handling,Electronic Components,Enclosures,Energy Management,Lab Ware and Clinical Diagnostics,Travel Suitcase,Wiring Devices,Wire & cable | |
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C | |