Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.26 g/cm³ Show Material materials with Dichte of 1.26 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.15 % Show Material materials with Wasserabsorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 3.5 GPa Show Material materials with Biegemodul of 3.5 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 6 % Show Material materials with Dehnung of 6 % | ASTM D 638 | Type I, 5 mm/min | ||
Elastizitätsmodul | 23.0 °C | 3.6 GPa Show Material materials with Elastizitätsmodul of 3.6 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural yield strength | 23.0 °C | 122 MPa Show Material materials with Flexural yield strength of 122 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 70 J/m Show Material materials with Impact strength, Izod notched, ASTM of 70 J/m | ASTM D 256 | ||
23.0 °C | 90 J/m Show Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 | |||
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1200 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 1200 J/m | ASTM D 4812 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA | ||
23.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | ||
23.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | |||
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 73 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 73 kJ/m² | ISO 180/1U | ||
Streckgrenze | 23.0 °C | 74 MPa Show Material materials with Streckgrenze of 74 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Zugfestigkeit | 23.0 °C | 62 MPa Show Material materials with Zugfestigkeit of 62 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 137 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 137 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 5E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 149 °C Show Material materials with Vicat-Erweichungstemperatur of 149 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.4E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94-5VB Rating | 3mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 175 V Show Material materials with Kriechstromfestigkeit of 175 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 8 g/10min Show Material materials with Schmelzmassenflussrate of 8 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schmelzvolumenflussrate | 7 cm³/10min Show Material materials with Schmelzvolumenflussrate of 7 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.4 - 0.6 % Show Material materials with Schrumpfung of 0.4 - 0.6 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine,Circuit Protection,Data Transfer,Displays,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,EV Infrastructure,Heavy Vehicles,Lab Ware and Clinical Diagnostics,LED Lighting,Medical Device,Monitoring and Imaging,Non-LED Lighting,Personal Computing,Power Boat,Power Manangement,Small Appliance,Wireless Communications,Wiring Devices | |
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C | |