Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.26 g/cm³ Show Material materials with Dichte of 1.26 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.13 % Show Material materials with Wasserabsorption of 0.13 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 3.52 GPa Show Material materials with Biegemodul of 3.52 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Dehnung | 23.0 °C | 12 % Show Material materials with Dehnung of 12 % | ASTM D 638 | Type I, 5 mm/min | ||
Elastizitätsmodul | 23.0 °C | 3.93 GPa Show Material materials with Elastizitätsmodul of 3.93 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural yield strength | 23.0 °C | 108 MPa Show Material materials with Flexural yield strength of 108 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Hardness, Rockwell R | 23.0 °C | 124 [-] Show Material materials with Hardness, Rockwell R of 124 [-] | ASTM D 785 | ||
Härte, Rockwell M | 23.0 °C | 85 [-] Show Material materials with Härte, Rockwell M of 85 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 106 J/m Show Material materials with Impact strength, Izod notched, ASTM of 106 J/m | ASTM D 256 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA | ||
23.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 130 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 130 kJ/m² | ISO 179/1eU | ||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | ||
23.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | |||
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 130 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 130 kJ/m² | ISO 180/1U | ||
Streckgrenze | 23.0 °C | 63 MPa Show Material materials with Streckgrenze of 63 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Zugfestigkeit | 23.0 °C | 48 MPa Show Material materials with Zugfestigkeit of 48 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 140 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 140 °C | ISO 75/Bf | 0.45 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 4.7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Spezifische Wärmekapazität | 23.0 °C | 1210 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 1210 J/(kg·K) | ASTM C 351 | ||
Vicat-Erweichungstemperatur | 143 °C Show Material materials with Vicat-Erweichungstemperatur of 143 °C | ISO 306 | Rate B/120 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ASTM C177 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.4E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 175 V Show Material materials with Kriechstromfestigkeit of 175 V | IEC 60112 |
spezifischer Widerstand | 23.0 °C | 1.00E+13 Ω·m Show Material materials with spezifischer Widerstand of 1.00E+13 Ω·m | IEC 60093 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 9 cm³/10min Show Material materials with Schmelzvolumenflussrate of 9 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.3 % Show Material materials with Schrumpfung of 0.3 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Energy Management | |
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C | |