Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.58 g/cm³ Show Material materials with Dichte of 1.58 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.05 % Show Material materials with Wasserabsorption of 0.05 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 210 MPa Show Material materials with Biegefestigkeit of 210 MPa | ISO 178 |
Biegemodul | 23.0 °C | 8.5 GPa Show Material materials with Biegemodul of 8.5 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Material materials with Dehnung of 2 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 9.95 GPa Show Material materials with Elastizitätsmodul of 9.95 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 165 MPa Show Material materials with Flexural yield strength of 165 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Hardness, Ball Indentation | 23.0 °C | 110 MPa Show Material materials with Hardness, Ball Indentation of 110 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 119 [-] Show Material materials with Hardness, Rockwell R of 119 [-] | ISO 2039-2 |
Impact strength, Izod notched, ASTM | -30.0 °C | 48 J/m Show Material materials with Impact strength, Izod notched, ASTM of 48 J/m | ASTM D 256 |
23.0 °C | 57 J/m Show Material materials with Impact strength, Izod notched, ASTM of 57 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 470 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 470 J/m | ASTM D 4812 |
23.0 °C | 480 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 480 J/m | ASTM D 4812 | |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA |
23.0 °C | 9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 40 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 45 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A |
23.0 °C | 8 - 9 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 - 9 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 40 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 40 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 45 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 115 MPa Show Material materials with Streckgrenze of 115 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 115 MPa Show Material materials with Zugfestigkeit of 115 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 190 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 190 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.5E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 202 °C Show Material materials with Vicat-Erweichungstemperatur of 202 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.5E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94HB Flame Class Rating | 1.6mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.3 [-] Show Material materials with Dielektrizitätskonstante of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 15 kV/mm Show Material materials with Durchschlagfestigkeit of 15 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Kriechstromfestigkeit | 23.0 °C | 300 V Show Material materials with Kriechstromfestigkeit of 300 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Material materials with Verlustfaktor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 15 g/10min Show Material materials with Schmelzmassenflussrate of 15 g/10min | ASTM D 1238 | 265°C/2.16kgf | |
Schmelzvolumenflussrate | 15 cm³/10min Show Material materials with Schmelzvolumenflussrate of 15 cm³/10min | ISO 1133 | 265°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.4 - 0.8 % Show Material materials with Schrumpfung of 0.4 - 0.8 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.6 - 1 % Show Material materials with Schrumpfung, diagonal of 0.6 - 1 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Door Handle,Exterior Mirror,Exterior Trim,Meter Gas,Motorcycle,Non-LED Lighting,Water Treatment/Filtration | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-285°C, Nozzle Temperature: 265-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 255-280°C, Rear - Zone 1 Temperature: 240-260°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-110°C | |