Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.03 g/cm³ Show Material materials with Dichte of 1.03 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 1.78 GPa Show Material materials with Biegemodul of 1.78 GPa | ISO 178 | 2 mm/min, 64mm | ||
Dehnung | 23.0 °C | 100.8 % Show Material materials with Dehnung of 100.8 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 1.89 GPa Show Material materials with Elastizitätsmodul of 1.89 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 4.7 % Show Material materials with Elongation at yield of 4.7 % | ASTM D 638 | Type I, 50 mm/min | ||
Härte, Shore D | 23.0 °C | 54 [-] Show Material materials with Härte, Shore D of 54 [-] | ISO 868 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 510 J/m Show Material materials with Impact strength, Izod notched, ASTM of 510 J/m | ASTM D 256 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA | ||
23.0 °C | 55 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 55 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 6 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 6 kJ/m² | ISO 180/1A | ||
23.0 °C | 47 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 47 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 17 MPa Show Material materials with Streckgrenze of 17 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 12 MPa Show Material materials with Zugfestigkeit of 12 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 53 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 53 °C | ASTM D 648 | 1.82 MPa, 3.2 mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3.2E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 3.2E-5 1/K | ISO 11359-2 | -30°C to 100°C |
Vicat-Erweichungstemperatur | 122 °C Show Material materials with Vicat-Erweichungstemperatur of 122 °C | ISO 306 | 10N, 50°C/hr | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.72E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.72E-4 1/K | ISO 11359-2 | -30°C to 100°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 21 g/10min Show Material materials with Schmelzmassenflussrate of 21 g/10min | ISO 1133 | 230°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.6 % Show Material materials with Schrumpfung of 0.6 % | SABIC method | 30 min, 120°C |
Schrumpfung, diagonal | 23.0 °C | 0.9 % Show Material materials with Schrumpfung, diagonal of 0.9 % | SABIC method | 30 min, 120°C |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Exterior,Recreational Vehicle | |
| Fillers | Mineral Powder | |
| Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa | |