Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.4 GPa Show Material materials with Biegemodul of 2.4 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Dehnung | 23.0 °C | 90 % Show Material materials with Dehnung of 90 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.4 GPa Show Material materials with Elastizitätsmodul of 2.4 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 700 J/m Show Material materials with Impact strength, Izod notched, ASTM of 700 J/m | ASTM D 256 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 14 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA | ||
23.0 °C | 15 - 68 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 - 68 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 13 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 13 kJ/m² | ISO 180/1A | ||
23.0 °C | 64 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 64 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 65 MPa Show Material materials with Streckgrenze of 65 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 65 MPa Show Material materials with Zugfestigkeit of 65 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75/Bf | 0.45 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 140 °C Show Material materials with Vicat-Erweichungstemperatur of 140 °C | ISO 306 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.2E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94V-0 Flame Class Rating | 2.5mm | UL 94 by SABIC-IP | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 27 g/10min Show Material materials with Schmelzmassenflussrate of 27 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schmelzvolumenflussrate | 26 cm³/10min Show Material materials with Schmelzvolumenflussrate of 26 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.3 % Show Material materials with Schrumpfung of 0.3 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.3 % Show Material materials with Schrumpfung, diagonal of 0.3 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Power Manangement,Wiring Devices | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 270-295°C, Nozzle Temperature: 265-290°C, Front - Zone 3 Temperature: 270-295°C, Middle - Zone 2 Temperature: 260-280°C, Rear - Zone 1 Temperature: 250-270°C, Mold Temperature: 70-95°C | |