Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.3 GPa Show Material materials with Biegemodul of 2.3 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 85 % Show Material materials with Dehnung of 85 % | ISO 527 | 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.35 GPa Show Material materials with Elastizitätsmodul of 2.35 GPa | ISO 527 | 1 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 14 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA | ||
23.0 °C | 73 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 73 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 12 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 70 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 70 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 63 MPa Show Material materials with Streckgrenze of 63 MPa | ISO 527 | 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 60 MPa Show Material materials with Zugfestigkeit of 60 MPa | ISO 527 | 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 124 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 124 °C | ISO 75/Ae | 1.8 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 142 °C Show Material materials with Vicat-Erweichungstemperatur of 142 °C | ISO 306 | Rate B/120 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ISO 8302 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.7 [-] Show Material materials with Dielektrizitätskonstante of 2.7 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 17 kV/mm Show Material materials with Durchschlagfestigkeit of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Material materials with Verlustfaktor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 14 cm³/10min Show Material materials with Schmelzvolumenflussrate of 14 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Air Cabin Interiors,ATM/Ticket Machine,Circuit Protection,Data Management,Data Transfer,Displays,Document Handling,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,EV Infrastructure,Freezer,Heavy Vehicles,Lab Ware and Clinical Diagnostics,LED Lighting,Medical Facility Infrastructure,Meter Water,Monitoring and Imaging,Non-LED Lighting,Personal Computing,Photo/Video Camera,Power Manangement,Recreational Vehicle,Security/Detection,Wireless Communications,Wiring Devices,Wire & cable | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-310°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-310°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-110°C | |