Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.05 g/cm³ Show Material materials with Dichte of 1.05 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.03 GPa Show Material materials with Biegemodul of 2.03 GPa | ISO 178 | 2 mm/min |
Elastizitätsmodul | 23.0 °C | 2.27 GPa Show Material materials with Elastizitätsmodul of 2.27 GPa | ASTM D 638 | 5 mm/min |
Flexural yield strength | 23.0 °C | 67 MPa Show Material materials with Flexural yield strength of 67 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 293 J/m Show Material materials with Impact strength, Izod notched, ASTM of 293 J/m | ASTM D 256 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A |
23.0 °C | 12 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 53 MPa Show Material materials with Streckgrenze of 53 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 95 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 95 °C | ISO 75/Bf | 0.45 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.35E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.35E-4 1/K | ASTM E 831 | -40°C to 60°C | ||
Vicat-Erweichungstemperatur | 98 °C Show Material materials with Vicat-Erweichungstemperatur of 98 °C | ISO 306 | Rate B/50 | |||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating | 1.52mm | UL 94 | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 23.0 °C | 163 Pa·s Show Material materials with Melt viscosity of 163 Pa·s | ASTM D 3825 | 260°C, 1000 sec⁻¹ |
Schmelzmassenflussrate | 14 g/10min Show Material materials with Schmelzmassenflussrate of 14 g/10min | ISO 1133 | 220°C/10.0 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.8 % Show Material materials with Schrumpfung of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Doors Hardware/Trim,Electronic Components,Energy Management,Forward Lighting,Headliner,Interior,Overhead,Recreational Vehicle,Scooter/Moped,Seat,Structure,Trim,Wireless Communications,Wiring Devices | |
| Processing methods | Drying Temperature: 90-95°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 230-275°C, Nozzle Temperature: 230-275°C, Front - Zone 3 Temperature: 220-255°C, Middle - Zone 2 Temperature: 210-250°C, Rear - Zone 1 Temperature: 195-240°C, Mold Temperature: 50-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm | |