Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.05 g/cm³ Show Material materials with Dichte of 1.05 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.41 GPa Show Material materials with Biegemodul of 2.41 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Elastizitätsmodul | 23.0 °C | 2.2 GPa Show Material materials with Elastizitätsmodul of 2.2 GPa | ASTM D 638 | 5 mm/min |
Flexural yield strength | 23.0 °C | 72 MPa Show Material materials with Flexural yield strength of 72 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 186 J/m Show Material materials with Impact strength, Izod notched, ASTM of 186 J/m | ASTM D 256 |
Streckgrenze | 23.0 °C | 48 MPa Show Material materials with Streckgrenze of 48 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 85 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 85 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.55E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.55E-4 1/K | ASTM E 831 | -40°C to 60°C | ||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating | 1.47mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 1 V Show Material materials with Kriechstromfestigkeit of 1 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 23.0 °C | 155 Pa·s Show Material materials with Melt viscosity of 155 Pa·s | ASTM D 3825 | 260°C, 1000 sec⁻¹ |
Schmelzmassenflussrate | 3.3 g/10min Show Material materials with Schmelzmassenflussrate of 3.3 g/10min | ASTM D 1238 | 230°C/3.8 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.8 % Show Material materials with Schrumpfung of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Doors Hardware/Trim,Electronic Components,Enclosure/Housing/Cover,Enclosures,Recreational Vehicle | |
| Processing methods | Drying Temperature: 90-95°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 230-275°C, Nozzle Temperature: 230-275°C, Front - Zone 3 Temperature: 220-255°C, Middle - Zone 2 Temperature: 210-250°C, Rear - Zone 1 Temperature: 195-240°C, Mold Temperature: 50-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm | |