Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.23 g/cm³ Show Material materials with Dichte of 1.23 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.15 % Show Material materials with Wasserabsorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 4.28 GPa Show Material materials with Biegemodul of 4.28 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 4 % Show Material materials with Dehnung of 4 % | ASTM D 638 | Type I, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 5.33 GPa Show Material materials with Elastizitätsmodul of 5.33 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 3.5 % Show Material materials with Elongation at yield of 3.5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 150 MPa Show Material materials with Flexural yield strength of 150 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 78 J/m Show Material materials with Impact strength, Izod notched, ASTM of 78 J/m | ASTM D 256 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/2C |
23.0 °C | 12 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/2C | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 100 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 100 kJ/m² | ISO 179/1eU |
23.0 °C | 100 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 100 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 80 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 80 kJ/m² | ISO 180/1U |
23.0 °C | 80 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 80 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 92 MPa Show Material materials with Streckgrenze of 92 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 91 MPa Show Material materials with Zugfestigkeit of 91 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 141 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 141 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 4E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Relative temperature index, electrical | 80 °C Show Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 148 °C Show Material materials with Vicat-Erweichungstemperatur of 148 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 4E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 4E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.2 [-] Show Material materials with Dielektrizitätskonstante of 3.2 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 20 kV/mm Show Material materials with Durchschlagfestigkeit of 20 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Kriechstromfestigkeit | 23.0 °C | 150 V Show Material materials with Kriechstromfestigkeit of 150 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Material materials with Verlustfaktor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 6.5 g/10min Show Material materials with Schmelzmassenflussrate of 6.5 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schmelzvolumenflussrate | 6 cm³/10min Show Material materials with Schmelzvolumenflussrate of 6 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.2 - 0.5 % Show Material materials with Schrumpfung of 0.2 - 0.5 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.2 - 0.5 % Show Material materials with Schrumpfung, diagonal of 0.2 - 0.5 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Displays,Document Handling,Electronic Components,LED Lighting,Personal Computing,Plumbing,Wireless Communications | |
| Fillers | 15% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C | |