Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.22 g/cm³ Show Material materials with Dichte of 1.22 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.2 % Show Material materials with Wasserabsorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 135 MPa Show Material materials with Biegefestigkeit of 135 MPa | ISO 178 |
Biegemodul | 23.0 °C | 4.25 GPa Show Material materials with Biegemodul of 4.25 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 3.2 % Show Material materials with Dehnung of 3.2 % | ISO 527 | 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.7 GPa Show Material materials with Elastizitätsmodul of 4.7 GPa | ISO 527 | 1 mm/min |
Elongation at yield | 23.0 °C | 3.2 % Show Material materials with Elongation at yield of 3.2 % | ISO 527 | 5 mm/min |
Flexural yield strength | 23.0 °C | 125 MPa Show Material materials with Flexural yield strength of 125 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 116 MPa Show Material materials with Hardness, Ball Indentation of 116 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 20 kJ/m² | ISO 180/1U |
Streckgrenze | 23.0 °C | 90 MPa Show Material materials with Streckgrenze of 90 MPa | ISO 527 | 5 mm/min |
Zugfestigkeit | 23.0 °C | 90 MPa Show Material materials with Zugfestigkeit of 90 MPa | ISO 527 | 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 123 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 123 °C | ISO 75/Ae | 1.8 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 4E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |
Vicat-Erweichungstemperatur | 136 °C Show Material materials with Vicat-Erweichungstemperatur of 136 °C | ISO 306 | Rate B/120 | |
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ISO 8302 |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 33 cm³/10min Show Material materials with Schmelzvolumenflussrate of 33 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.3 - 0.5 % Show Material materials with Schrumpfung of 0.3 - 0.5 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Doors Hardware/Trim,Medical Device,Pharmaceutical Packaging & Drug Delivery,Seat,Trim,Wireless Communications | |
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Temperature: 100-110°C, Drying Time: 2-4hrs, Melt Temperature: 240-280°C, Mold Temperature: 50-80°C | |