Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.22 g/cm³ Show Material materials with Dichte of 1.22 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.15 % Show Material materials with Wasserabsorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2 GPa Show Material materials with Biegemodul of 2 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 50 % Show Material materials with Dehnung of 50 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.05 GPa Show Material materials with Elastizitätsmodul of 2.05 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 75 MPa Show Material materials with Flexural yield strength of 75 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 82 MPa Show Material materials with Hardness, Ball Indentation of 82 MPa | ISO 2039-1 | ||
Hardness, Rockwell L | 23.0 °C | 89 [-] Show Material materials with Hardness, Rockwell L of 89 [-] | ISO 2039-2 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 450 J/m Show Material materials with Impact strength, Izod notched, ASTM of 450 J/m | ASTM D 256 | ||
23.0 °C | 625 J/m Show Material materials with Impact strength, Izod notched, ASTM of 625 J/m | ASTM D 256 | |||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 20 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | ISO 179/2C | ||
-20.0 °C | 25 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 25 kJ/m² | ISO 179/2C | |||
23.0 °C | 30 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 30 kJ/m² | ISO 179/2C | |||
Schlagzähigkeit, Izod gekerbt | -40.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 25 kJ/m² | ISO 180/1A | ||
-30.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 35 kJ/m² | ISO 180/1A | |||
23.0 °C | 50 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 50 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 53 MPa Show Material materials with Streckgrenze of 53 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 49 MPa Show Material materials with Zugfestigkeit of 49 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 83 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 83 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 120 °C Show Material materials with Vicat-Erweichungstemperatur of 120 °C | ASTM D 1525 | Rate B/50 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.18 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.18 W/(m·K) | ISO 8302 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9.5E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 9.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.3 [-] Show Material materials with Dielektrizitätskonstante of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 17 kV/mm Show Material materials with Durchschlagfestigkeit of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Verlustfaktor | 23.0 °C | 0.02 [-] Show Material materials with Verlustfaktor of 0.02 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 14 g/10min Show Material materials with Schmelzmassenflussrate of 14 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Schmelzvolumenflussrate | 13 cm³/10min Show Material materials with Schmelzvolumenflussrate of 13 cm³/10min | ISO 1133 | 250°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.7 - 1.1 % Show Material materials with Schrumpfung of 0.7 - 1.1 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.7 - 1.1 % Show Material materials with Schrumpfung, diagonal of 0.7 - 1.1 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Applique,Auto Aftermarket,Electronic Components,Exterior Trim,Heavy Vehicles,Laundry Dryer,Meter Gas,Recreational Vehicle | |
| Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C | |