Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 4.51 GPa Show Material materials with Biegemodul of 4.51 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 35 % Show Material materials with Dehnung of 35 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.35 GPa Show Material materials with Elastizitätsmodul of 4.35 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 101 MPa Show Material materials with Flexural yield strength of 101 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 60 J/m Show Material materials with Impact strength, Izod notched, ASTM of 60 J/m | ASTM D 256 |
23.0 °C | 86 J/m Show Material materials with Impact strength, Izod notched, ASTM of 86 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A |
23.0 °C | 7 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 55 MPa Show Material materials with Streckgrenze of 55 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 90 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 4.9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 97 °C Show Material materials with Vicat-Erweichungstemperatur of 97 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.4E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94-5VB Rating | 1.5mm | UL 94 by SABIC-IP | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 16.5 g/10min Show Material materials with Schmelzmassenflussrate of 16.5 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Schmelzvolumenflussrate | 15 cm³/10min Show Material materials with Schmelzvolumenflussrate of 15 cm³/10min | ISO 1133 | 260°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.33 % Show Material materials with Schrumpfung of 0.33 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.38 % Show Material materials with Schrumpfung, diagonal of 0.38 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Data Management,Personal Computing,Wireless Communications | |
| Fillers | Mineral Powder | |
| Processing methods | Drying Temperature: 80-90°C, Drying Time (Cumulative): 16hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 255-285°C, Nozzle Temperature: 255-285°C, Front - Zone 3 Temperature: 255-285°C, Middle - Zone 2 Temperature: 230-275°C, Rear - Zone 1 Temperature: 220-255°C, Mold Temperature: 70-95°C | |