Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.18 g/cm³ Show Material materials with Dichte of 1.18 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.2 % Show Material materials with Wasserabsorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.44 GPa Show Material materials with Biegemodul of 2.44 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 65 % Show Material materials with Dehnung of 65 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.76 GPa Show Material materials with Elastizitätsmodul of 2.76 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 4.1 % Show Material materials with Elongation at yield of 4.1 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 94 MPa Show Material materials with Flexural yield strength of 94 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 100 J/m Show Material materials with Impact strength, Izod notched, ASTM of 100 J/m | ASTM D 256 | ||
23.0 °C | 475 J/m Show Material materials with Impact strength, Izod notched, ASTM of 475 J/m | ASTM D 256 | |||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 33 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 33 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 12 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 25 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 63 MPa Show Material materials with Streckgrenze of 63 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 47 MPa Show Material materials with Zugfestigkeit of 47 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 98 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 98 °C | ISO 75/Bf | 0.45 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Relative temperature index, electrical | 85 °C Show Material materials with Relative temperature index, electrical of 85 °C | UL 746B | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 106 °C Show Material materials with Vicat-Erweichungstemperatur of 106 °C | ISO 306 | Rate B/120 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94V-0 Flame Class Rating | 1.5mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.9 [-] Show Material materials with Dielektrizitätskonstante of 2.9 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 31 kV/mm Show Material materials with Durchschlagfestigkeit of 31 kV/mm | IEC 60243-1 | in oil, 1.6 mm |
Kriechstromfestigkeit | 23.0 °C | 0 V Show Material materials with Kriechstromfestigkeit of 0 V | UL 746A |
Verlustfaktor | 23.0 °C | 7E-3 [-] Show Material materials with Verlustfaktor of 7E-3 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 23 cm³/10min Show Material materials with Schmelzvolumenflussrate of 23 cm³/10min | ISO 1133 | 260°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.4 - 0.6 % Show Material materials with Schrumpfung of 0.4 - 0.6 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine,Coffee Maker/Espresso Machine,Dishwasher,Displays,Electronic Components,Enclosures,Freezer,Medical Device,Non-LED Lighting,Refrigerator | |
| Processing methods | Drying Temperature: 80-90°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-300°C, Nozzle Temperature: 250-300°C, Front - Zone 3 Temperature: 250-300°C, Middle - Zone 2 Temperature: 240-290°C, Rear - Zone 1 Temperature: 230-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-85°C, Vent Depth: 0.03-0.075mm | |