Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.18 g/cm³ Show Material materials with Dichte of 1.18 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.1 % Show Material materials with Wasserabsorption of 0.1 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.47 GPa Show Material materials with Biegemodul of 2.47 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 85 % Show Material materials with Dehnung of 85 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.33 GPa Show Material materials with Elastizitätsmodul of 2.33 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 96 MPa Show Material materials with Flexural yield strength of 96 MPa | ISO 178 | 2 mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 12 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA | ||
23.0 °C | 20 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 12 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 50 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 50 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 64 MPa Show Material materials with Streckgrenze of 64 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 62 MPa Show Material materials with Zugfestigkeit of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 118 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 95 °C Show Material materials with Relative temperature index, mechanical impact of 95 °C | UL 746B | |||
Relative temperature index, mechanical strength | 100 °C Show Material materials with Relative temperature index, mechanical strength of 100 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 134 °C Show Material materials with Vicat-Erweichungstemperatur of 134 °C | ISO 306 | Rate B/120 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94-5VB Flame Class Rating | 2.5mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.95 [-] Show Material materials with Dielektrizitätskonstante of 2.95 [-] | ASTM D 150 | at 1 MHz |
Kriechstromfestigkeit | 23.0 °C | 3 V Show Material materials with Kriechstromfestigkeit of 3 V | UL 746A |
Surface resistivity | 23.0 °C | 4.00E+16 Ω/sq Show Material materials with Surface resistivity of 4.00E+16 Ω/sq | IEC 60093 | ROA |
Verlustfaktor | 23.0 °C | 8.8E-3 [-] Show Material materials with Verlustfaktor of 8.8E-3 [-] | ASTM D 150 | at 1 MHz |
spezifischer Widerstand | 23.0 °C | 1.00E+13 Ω·m Show Material materials with spezifischer Widerstand of 1.00E+13 Ω·m | IEC 60093 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 13 cm³/10min Show Material materials with Schmelzvolumenflussrate of 13 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.4 - 0.8 % Show Material materials with Schrumpfung of 0.4 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Circuit Protection,Cooking Range,Data Transfer,Displays,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,EV Infrastructure,LED Lighting,Medical Device,Microwave Oven,Monitoring and Imaging,Non-LED Lighting,Personal Computing,Photovoltaic Components,Power Manangement,Refrigerator,Small Appliance,Wireless Communications | |
| Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-300°C, Nozzle Temperature: 230-290°C, Front - Zone 3 Temperature: 240-300°C, Middle - Zone 2 Temperature: 230-290°C, Rear - Zone 1 Temperature: 210-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C | |