Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Material materials with Dichte of 1.19 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.16 % Show Material materials with Wasserabsorption of 0.16 % | ASTM D 570 | 24 Hours |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.03 GPa Show Material materials with Biegemodul of 2.03 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 110 % Show Material materials with Dehnung of 110 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 81 MPa Show Material materials with Flexural yield strength of 81 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 694 J/m Show Material materials with Impact strength, Izod notched, ASTM of 694 J/m | ASTM D 256 |
23.0 °C | 694 - 774 J/m Show Material materials with Impact strength, Izod notched, ASTM of 694 - 774 J/m | ASTM D 256 | |
Streckgrenze | 23.0 °C | 57 MPa Show Material materials with Streckgrenze of 57 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 127 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.48E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.48E-5 1/K | ASTM E 831 | -40°C to 95°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 13 g/10min Show Material materials with Schmelzmassenflussrate of 13 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Cluster,Glove Box,Recreational Vehicle,Trim | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 295-315°C, Nozzle Temperature: 290-310°C, Front - Zone 3 Temperature: 295-315°C, Middle - Zone 2 Temperature: 280-305°C, Rear - Zone 1 Temperature: 270-295°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |