Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.25 g/cm³ Show Material materials with Dichte of 1.25 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.13 % Show Material materials with Wasserabsorption of 0.13 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.35 GPa Show Material materials with Biegemodul of 2.35 GPa | ISO 178 | 2 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.35 GPa Show Material materials with Elastizitätsmodul of 2.35 GPa | ISO 527 | 1 mm/min | ||
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 95 MPa Show Material materials with Flexural yield strength of 95 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 11 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 11 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 11 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 65 MPa Show Material materials with Streckgrenze of 65 MPa | ISO 527 | 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 70 MPa Show Material materials with Zugfestigkeit of 70 MPa | ISO 527 | 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 135 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 135 °C | ISO 75/Ae | 1.8 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Vicat-Erweichungstemperatur | 156 °C Show Material materials with Vicat-Erweichungstemperatur of 156 °C | ISO 306 | Rate B/120 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ISO 8302 | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.7 [-] Show Material materials with Dielektrizitätskonstante of 2.7 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 17 kV/mm Show Material materials with Durchschlagfestigkeit of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Material materials with Verlustfaktor of 0.01 [-] | IEC 60250 | at 1 MHz |
Optisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 5 cm³/10min Show Material materials with Schmelzvolumenflussrate of 5 cm³/10min | ISO 1133 | 300°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.4 - 0.6 % Show Material materials with Schrumpfung of 0.4 - 0.6 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Building/Construction Sheet,Enclosures,LED Lighting,Non-LED Lighting,Rail Cabin Interiors | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Barrel - Zone 1 Temperature: 260-300°C, Barrel - Zone 2 Temperature: 260-290°C, Barrel - Zone 3 Temperature: 260-290°C, Hopper Temperature: 100-120°C, Adapter Temperature: 240-280°C, Die Temperature: 240-300°C, Melt Temperature: 260-300°C | |