Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.2 g/cm³ Show Material materials with Dichte of 1.2 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.68 GPa Show Material materials with Biegemodul of 2.68 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 30 % Show Material materials with Dehnung of 30 % | ASTM D 638 | Type I, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.81 GPa Show Material materials with Elastizitätsmodul of 2.81 GPa | ASTM D 638 | 50 mm/min |
Elongation at yield | 23.0 °C | 5.7 % Show Material materials with Elongation at yield of 5.7 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 91 MPa Show Material materials with Flexural yield strength of 91 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 137 J/m Show Material materials with Impact strength, Izod notched, ASTM of 137 J/m | ASTM D 256 |
23.0 °C | 520 J/m Show Material materials with Impact strength, Izod notched, ASTM of 520 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 16 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 16 kJ/m² | ISO 179/1eA |
23.0 °C | 31 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 31 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 313 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 313 kJ/m² | ISO 179/1eU |
23.0 °C | 335 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 335 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 12 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A |
23.0 °C | 27 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 27 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 172 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 172 kJ/m² | ISO 180/1U |
23.0 °C | 171 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 171 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 58 MPa Show Material materials with Streckgrenze of 58 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 47 MPa Show Material materials with Zugfestigkeit of 47 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 145 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 145 °C | ISO 75/Bf | 0.45 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 5.4E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 5.4E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Vicat-Erweichungstemperatur | 148 °C Show Material materials with Vicat-Erweichungstemperatur of 148 °C | ASTM D 1525 | Rate A/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Entflammbarkeit | UL Recognized, 94-5VA Flame Class Rating | 6mm | UL 94 | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 3.2 g/10min Show Material materials with Schmelzmassenflussrate of 3.2 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schmelzvolumenflussrate | 3 cm³/10min Show Material materials with Schmelzvolumenflussrate of 3 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.6 % Show Material materials with Schrumpfung of 0.6 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.5 % Show Material materials with Schrumpfung, diagonal of 0.5 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Window | |
| Fillers | 5% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: .02%, Melt Temperature: 295-315°C, Nozzle Temperature: 290-310°C, Front - Zone 3 Temperature: 295-315°C, Middle - Zone 2 Temperature: 280-305°C, Rear - Zone 1 Temperature: 270-295°C, Mold Temperature: 70-95°C, Back Pressure: .3-.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: .02-.076mm | |