| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Material materials with Dichte of 1.19 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.26 GPa Show Material materials with Biegemodul of 2.26 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 17 % Show Material materials with Dehnung of 17 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.06 GPa Show Material materials with Elastizitätsmodul of 2.06 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 2.4 % Show Material materials with Elongation at yield of 2.4 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 63 MPa Show Material materials with Flexural yield strength of 63 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 213 J/m Show Material materials with Impact strength, Izod notched, ASTM of 213 J/m | ASTM D 256 |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 12 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A |
Streckgrenze | 23.0 °C | 37 MPa Show Material materials with Streckgrenze of 37 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 30 MPa Show Material materials with Zugfestigkeit of 30 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 75 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 75 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 93 °C Show Material materials with Vicat-Erweichungstemperatur of 93 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9.18E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 9.18E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94-5VA Flame Class Rating | 2.79mm | UL 94 | ||||
Elektrisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 23.0 °C | 320 Pa·s Show Material materials with Melt viscosity of 320 Pa·s | ASTM D 3825 | 200°C, 1000 sec⁻¹ |
Schmelzmassenflussrate | 7 g/10min Show Material materials with Schmelzmassenflussrate of 7 g/10min | ISO 1133 | 220°C/5.0 kg | |
Schmelzvolumenflussrate | 40 cm³/10min Show Material materials with Schmelzvolumenflussrate of 40 cm³/10min | ISO 1133 | 220°C/10.0 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Aerospace,Air Cabin Interiors,Air Conditioning,ATM/Ticket Machine,Audio,Auto Aftermarket,Building Accessory,Building/Construction Sheet,Coffee Maker/Espresso Machine,Conveyor,Data Management,Data Transfer,Displays,Document Handling,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,Food Processor,Headliner,Heavy Vehicles,Lab Ware and Clinical Diagnostics,Laundry Dryer,Lawn/Garden,LED Lighting,Medical Device,Medical Facility Infrastructure,Monitoring and Imaging,Non-LED Lighting,Oil/Gas,Personal Computing,Photovoltaic Components,Pump,Refrigerator,Renal and Blood Handling,Security/Detection,Small Appliance,Surgical Devices,Vacuum Cleaner,Vending Machine,Washing Machine,Wireless Communications,Wiring Devices | |
| Processing methods | Drying Temperature: 80-90°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 205-230°C, Nozzle Temperature: 205-230°C, Front - Zone 3 Temperature: 205-220°C, Middle - Zone 2 Temperature: 200-210°C, Rear - Zone 1 Temperature: 170-180°C, Mold Temperature: 50-70°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm | |