Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.11 g/cm³ Show Material materials with Dichte of 1.11 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.2 % Show Material materials with Wasserabsorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 2.5 GPa Show Material materials with Biegemodul of 2.5 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 18 % Show Material materials with Dehnung of 18 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.46 GPa Show Material materials with Elastizitätsmodul of 2.46 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 2.5 % Show Material materials with Elongation at yield of 2.5 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 64 MPa Show Material materials with Flexural yield strength of 64 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 23 J/m Show Material materials with Impact strength, Izod notched, ASTM of 23 J/m | ASTM D 256 |
23.0 °C | 140 J/m Show Material materials with Impact strength, Izod notched, ASTM of 140 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 2 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 2 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 43 MPa Show Material materials with Streckgrenze of 43 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 36 MPa Show Material materials with Zugfestigkeit of 36 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 84 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 84 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8.4E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8.4E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 98 °C Show Material materials with Vicat-Erweichungstemperatur of 98 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9.4E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 9.4E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 12 g/10min Show Material materials with Schmelzmassenflussrate of 12 g/10min | ASTM D 1238 | 220°C/10 kg | |
Schmelzvolumenflussrate | 13 cm³/10min Show Material materials with Schmelzvolumenflussrate of 13 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.4 - 0.7 % Show Material materials with Schrumpfung of 0.4 - 0.7 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.4 - 0.7 % Show Material materials with Schrumpfung, diagonal of 0.4 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Front Grille,Overhead | |
Processing methods | Drying Temperature: 85-90°C, Drying Time: 4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 240-270°C, Nozzle Temperature: 220-255°C, Front - Zone 3 Temperature: 230-260°C, Middle - Zone 2 Temperature: 220-255°C, Rear - Zone 1 Temperature: 215-250°C, Mold Temperature: 60-85°C, Back Pressure: 0.3-1MPa, Screw Speed: 30-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.038-0.076mm |