Eigenschaften
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.14 GPa Show Material materials with Biegemodul of 2.14 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 93 % Show Material materials with Dehnung of 93 % | ASTM D 638 | Type I, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.25 GPa Show Material materials with Elastizitätsmodul of 2.25 GPa | ASTM D 638 | 50 mm/min |
Elongation at yield | 23.0 °C | 4.8 % Show Material materials with Elongation at yield of 4.8 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 81 MPa Show Material materials with Flexural yield strength of 81 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 425 J/m Show Material materials with Impact strength, Izod notched, ASTM of 425 J/m | ASTM D 256 |
23.0 °C | 583 J/m Show Material materials with Impact strength, Izod notched, ASTM of 583 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 56 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 56 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 37 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 37 kJ/m² | ISO 180/1A |
23.0 °C | 40 - 45 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 40 - 45 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 53 MPa Show Material materials with Streckgrenze of 53 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 45 MPa Show Material materials with Zugfestigkeit of 45 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Schmelzmassenflussrate | 17 g/10min Show Material materials with Schmelzmassenflussrate of 17 g/10min | ASTM D 1238 | 260°C/5.0 kgf |
Schmelzvolumenflussrate | 18 cm³/10min Show Material materials with Schmelzvolumenflussrate of 18 cm³/10min | ISO 1133 | 260°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Pharmaceutical Packaging & Drug Delivery | |
| Processing methods | Drying Temperature: 100-110°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 240-280°C, Front - Zone 3 Temperature: 250-290°C, Middle - Zone 2 Temperature: 250-290°C, Rear - Zone 1 Temperature: 230-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C | |