Allgemein
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.3 GPa Show Material materials with Biegemodul of 2.3 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 110 % Show Material materials with Dehnung of 110 % | ISO 527 | 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.35 GPa Show Material materials with Elastizitätsmodul of 2.35 GPa | ISO 527 | 1 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 35 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 35 kJ/m² | ISO 179/2C | ||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 12 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 70 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 70 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 63 MPa Show Material materials with Streckgrenze of 63 MPa | ISO 527 | 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 70 MPa Show Material materials with Zugfestigkeit of 70 MPa | ISO 527 | 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 120 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 120 °C | ISO 75/Ae | 1.8 MPa |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B |
Vicat-Erweichungstemperatur | 140 °C Show Material materials with Vicat-Erweichungstemperatur of 140 °C | ISO 306 | Rate B/120 |
Optisch
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 17 cm³/10min Show Material materials with Schmelzvolumenflussrate of 17 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Renal and Blood Handling | |
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-310°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-310°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-110°C |