Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.2 GPa Show Material materials with Biegemodul of 2.2 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 125 % Show Material materials with Dehnung of 125 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.27 GPa Show Material materials with Elastizitätsmodul of 2.27 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6.5 % Show Material materials with Elongation at yield of 6.5 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 95 MPa Show Material materials with Flexural yield strength of 95 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 785 J/m Show Material materials with Impact strength, Izod notched, ASTM of 785 J/m | ASTM D 256 | ||
23.0 °C | 935 J/m Show Material materials with Impact strength, Izod notched, ASTM of 935 J/m | ASTM D 256 | |||
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2700 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 2700 J/m | ASTM D 4812 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 15 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/1eA | ||
23.0 °C | 75 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 75 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 15 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 15 kJ/m² | ISO 180/1A | ||
23.0 °C | 75 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 75 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 72 MPa Show Material materials with Zugfestigkeit of 72 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 132 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 132 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.6E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 145 °C Show Material materials with Vicat-Erweichungstemperatur of 145 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.5E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.5E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 24 g/10min Show Material materials with Schmelzmassenflussrate of 24 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Schmelzvolumenflussrate | 5 cm³/10min Show Material materials with Schmelzvolumenflussrate of 5 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung, diagonal of 0.5 - 0.7 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine,Fluid Delivery,Medical Device,Oil/Gas,Surgical Devices | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 310-330°C, Nozzle Temperature: 305-325°C, Front - Zone 3 Temperature: 310-330°C, Middle - Zone 2 Temperature: 300-320°C, Rear - Zone 1 Temperature: 290-310°C, Mold Temperature: 80-115°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |