Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.16 g/cm³ Show Material materials with Dichte of 1.16 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.1 GPa Show Material materials with Biegemodul of 2.1 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 160 % Show Material materials with Dehnung of 160 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.16 GPa Show Material materials with Elastizitätsmodul of 2.16 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 80 MPa Show Material materials with Flexural yield strength of 80 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 63 MPa Show Material materials with Hardness, Ball Indentation of 63 MPa | ISO 2039-1 |
Hardness, Rockwell L | 23.0 °C | 57 [-] Show Material materials with Hardness, Rockwell L of 57 [-] | ISO 2039-2 |
Härte, Shore D | 23.0 °C | 77 [-] Show Material materials with Härte, Shore D of 77 [-] | ISO 868 |
Impact strength, Izod notched, ASTM | -30.0 °C | 140 J/m Show Material materials with Impact strength, Izod notched, ASTM of 140 J/m | ASTM D 256 |
23.0 °C | 450 J/m Show Material materials with Impact strength, Izod notched, ASTM of 450 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 17 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 17 kJ/m² | ISO 179/1eA |
23.0 °C | 45 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 45 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 14 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 14 kJ/m² | ISO 180/1A |
23.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 45 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 50 MPa Show Material materials with Streckgrenze of 50 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 58 MPa Show Material materials with Zugfestigkeit of 58 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq | IEC 60093 | ROA |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Schmelzmassenflussrate | 8 g/10min Show Material materials with Schmelzmassenflussrate of 8 g/10min | ISO 1133 | 220°C/10.0 kg |
Schmelzvolumenflussrate | 29 cm³/10min Show Material materials with Schmelzvolumenflussrate of 29 cm³/10min | ISO 1133 | 260°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Overhead | |
| Processing methods | Drying Temperature: 85-95°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 255-270°C, Nozzle Temperature: 235-255°C, Front - Zone 3 Temperature: 245-260°C, Middle - Zone 2 Temperature: 235-255°C, Rear - Zone 1 Temperature: 230-250°C, Mold Temperature: 60-85°C, Back Pressure: 0.3-1MPa, Screw Speed: 30-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.038-0.076mm | |