Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.15 g/cm³ Show Material materials with Dichte of 1.15 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.2 % Show Material materials with Wasserabsorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.4 GPa Show Material materials with Biegemodul of 2.4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 125 % Show Material materials with Dehnung of 125 % | ISO 527 | 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.5 GPa Show Material materials with Elastizitätsmodul of 2.5 GPa | ISO 527 | 1 mm/min |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ISO 527 | 50 mm/min |
Flexural yield strength | 23.0 °C | 85 MPa Show Material materials with Flexural yield strength of 85 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 106 MPa Show Material materials with Hardness, Ball Indentation of 106 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 12 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA |
23.0 °C | 45 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 45 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 15 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 15 kJ/m² | ISO 180/1A |
23.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 45 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | ISO 527 | 50 mm/min |
Zugfestigkeit | 23.0 °C | 62 MPa Show Material materials with Zugfestigkeit of 62 MPa | ISO 527 | 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 114 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 114 °C | ISO 75/Ae | 1.8 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Vicat-Erweichungstemperatur | 134 °C Show Material materials with Vicat-Erweichungstemperatur of 134 °C | ISO 306 | Rate B/120 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ISO 8302 | ||
Entflammbarkeit | UL Compliant, 94HB Flame Class Rating | 1.6mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.8 [-] Show Material materials with Dielektrizitätskonstante of 2.8 [-] | IEC 60250 | at 1 MHz |
Durchschlagfestigkeit | 23.0 °C | 17 kV/mm Show Material materials with Durchschlagfestigkeit of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Kriechstromfestigkeit | 23.0 °C | 225 V Show Material materials with Kriechstromfestigkeit of 225 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Material materials with Verlustfaktor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 17 cm³/10min Show Material materials with Schmelzvolumenflussrate of 17 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.4 - 0.6 % Show Material materials with Schrumpfung of 0.4 - 0.6 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components,Enclosures,Heavy Vehicles,Wiring Devices | |
| Processing methods | Drying Temperature: 100-110°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 240-280°C, Front - Zone 3 Temperature: 250-290°C, Middle - Zone 2 Temperature: 250-290°C, Rear - Zone 1 Temperature: 230-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C | |