Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.08 g/cm³ Show Material materials with Dichte of 1.08 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 3.46 GPa Show Material materials with Biegemodul of 3.46 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 92 MPa Show Material materials with Flexural yield strength of 92 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 46 J/m Show Material materials with Impact strength, Izod notched, ASTM of 46 J/m | ASTM D 256 |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 1 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 1 kJ/m² | ISO 179/2C |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 2 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 2 kJ/m² | ISO 180/1A |
23.0 °C | 3 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 3 kJ/m² | ISO 180/1A | |
Thermisch
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Schmelzmassenflussrate | 16 g/10min Show Material materials with Schmelzmassenflussrate of 16 g/10min | ISO 1133 | 220°C/10.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Additive Plastic | |
| Processing methods | Drying Temperature: 75-85°C, Drying Time (Cumulative): 2-4hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 190-220°C, Nozzle Temperature: 190-220°C, Front - Zone 3 Temperature: 190-210°C, Middle - Zone 2 Temperature: 180-200°C, Rear - Zone 1 Temperature: 170-190°C, Mold Temperature: 50-70°C, Screw Speed: 40-70rpm | |