Allgemein
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.3 GPa Show Material materials with Biegemodul of 2.3 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 130 % Show Material materials with Dehnung of 130 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.41 GPa Show Material materials with Elastizitätsmodul of 2.41 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 800 J/m Show Material materials with Impact strength, Izod notched, ASTM of 800 J/m | ASTM D 256 | ||
Impact strength, Izod unnotched, ASTM | 23.0 °C | 3204 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 | ||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 12 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 63 MPa Show Material materials with Streckgrenze of 63 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 68 MPa Show Material materials with Zugfestigkeit of 68 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No break @ 23°C | ISO 179/2C |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 132 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 132 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.84E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.84E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 154 °C Show Material materials with Vicat-Erweichungstemperatur of 154 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.65E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.65E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 10.5 g/10min Show Material materials with Schmelzmassenflussrate of 10.5 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schmelzvolumenflussrate | 9 cm³/10min Show Material materials with Schmelzvolumenflussrate of 9 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Additive Semiconductor Materials,Building/Construction Sheet,Vacuum Cleaner | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 295-315°C, Nozzle Temperature: 290-310°C, Front - Zone 3 Temperature: 295-315°C, Middle - Zone 2 Temperature: 280-305°C, Rear - Zone 1 Temperature: 270-295°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm |