Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.34 g/cm³ Show Material materials with Dichte of 1.34 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.15 % Show Material materials with Wasserabsorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.5 GPa Show Material materials with Biegemodul of 2.5 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 74 % Show Material materials with Dehnung of 74 % | ASTM D 638 | Type I, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.5 GPa Show Material materials with Elastizitätsmodul of 2.5 GPa | ISO 527 | 1 mm/min |
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 135 J/m Show Material materials with Impact strength, Izod notched, ASTM of 135 J/m | ASTM D 256 |
23.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2130 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 2130 J/m | ASTM D 4812 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 60 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 60 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 140 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 140 kJ/m² | ISO 179/1eU |
23.0 °C | 140 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 140 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 42 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 42 kJ/m² | ISO 180/1A |
23.0 °C | 64 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 64 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 175 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 175 kJ/m² | ISO 180/1U |
23.0 °C | 180 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 180 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 57 MPa Show Material materials with Streckgrenze of 57 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 50 MPa Show Material materials with Zugfestigkeit of 50 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 129 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.1E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.1E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 147 °C Show Material materials with Vicat-Erweichungstemperatur of 147 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.4E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94V-2 Flame Class Rating | 1.5mm | UL 94 | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 7.5 g/10min Show Material materials with Schmelzmassenflussrate of 7.5 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.8 - 1 % Show Material materials with Schrumpfung of 0.8 - 1 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | LED Lighting,Non-LED Lighting | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 310-330°C, Nozzle Temperature: 305-325°C, Front - Zone 3 Temperature: 310-330°C, Middle - Zone 2 Temperature: 300-320°C, Rear - Zone 1 Temperature: 290-310°C, Mold Temperature: 80-115°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm, Drying Temperature: 120°C, Drying Time: 2-4hrs, Barrel - Zone 1 Temperature: 240-285°C, Barrel - Zone 2 Temperature: 240-285°C, Barrel - Zone 3 Temperature: 240-285°C, Hopper Temperature: 100-120°C, Adapter Temperature: 230-285°C, Die Temperature: 230-295°C, Melt Temperature: 240-295°C | |