Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.38 g/cm³ Show Material materials with Dichte of 1.38 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.22 % Show Material materials with Wasserabsorption of 0.22 % | ISO 62 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.7 GPa Show Material materials with Biegemodul of 2.7 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Dehnung | 23.0 °C | 75 % Show Material materials with Dehnung of 75 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.75 GPa Show Material materials with Elastizitätsmodul of 2.75 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 | ||
Härte, Rockwell M | 23.0 °C | 46 [-] Show Material materials with Härte, Rockwell M of 46 [-] | ISO 2039-2 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 400 J/m Show Material materials with Impact strength, Izod notched, ASTM of 400 J/m | ASTM D 256 | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 40 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 40 kJ/m² | ISO 179/1eA | ||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 25 kJ/m² | ISO 180/1A | ||
23.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 35 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 55 MPa Show Material materials with Streckgrenze of 55 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 50 MPa Show Material materials with Zugfestigkeit of 50 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75/Bf | 0.45 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 143 °C Show Material materials with Vicat-Erweichungstemperatur of 143 °C | ISO 306 | Rate B/120 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94-5VA Flame Class Rating | 3mm | UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 275 V Show Material materials with Kriechstromfestigkeit of 275 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 19 cm³/10min Show Material materials with Schmelzvolumenflussrate of 19 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.3 - 0.5 % Show Material materials with Schrumpfung of 0.3 - 0.5 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.3 - 0.5 % Show Material materials with Schrumpfung, diagonal of 0.3 - 0.5 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosures,Heavy Vehicles,LED Lighting | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 270-295°C, Nozzle Temperature: 265-290°C, Front - Zone 3 Temperature: 270-295°C, Middle - Zone 2 Temperature: 260-280°C, Rear - Zone 1 Temperature: 250-270°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm |