Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.05 g/cm³ Show Material materials with Dichte of 1.05 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.2 % Show Material materials with Wasserabsorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 2.31 GPa Show Material materials with Biegemodul of 2.31 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 98 % Show Material materials with Dehnung of 98 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.39 GPa Show Material materials with Elastizitätsmodul of 2.39 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 2.9 % Show Material materials with Elongation at yield of 2.9 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 70 MPa Show Material materials with Flexural yield strength of 70 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 374 J/m Show Material materials with Impact strength, Izod notched, ASTM of 374 J/m | ASTM D 256 |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 27 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 27 kJ/m² | ISO 180/1A |
Streckgrenze | 23.0 °C | 43 MPa Show Material materials with Streckgrenze of 43 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 36 MPa Show Material materials with Zugfestigkeit of 36 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 82 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 82 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8.82E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8.82E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 98 °C Show Material materials with Vicat-Erweichungstemperatur of 98 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.64E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.64E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating | 1.5mm | UL 94 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 15 g/10min Show Material materials with Schmelzmassenflussrate of 15 g/10min | ISO 1133 | 220°C/10.0 kg | |
Schmelzvolumenflussrate | 5 cm³/10min Show Material materials with Schmelzvolumenflussrate of 5 cm³/10min | ISO 1133 | 220°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.8 % Show Material materials with Schrumpfung of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Amusement Machine,Building Accessory,Electronic Components,Enclosure/Housing/Cover,Enclosures,Freezer,Heavy Vehicles,Laundry Dryer,Non-LED Lighting,Refrigerator,Security/Detection,Swimming Pool/Spa,Vending Machine,Washing Machine,Wearables,Wiring Devices | |
Processing methods | Drying Temperature: 80-95°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 220-260°C, Nozzle Temperature: 220-260°C, Front - Zone 3 Temperature: 215-240°C, Middle - Zone 2 Temperature: 205-225°C, Rear - Zone 1 Temperature: 190-210°C, Mold Temperature: 50-70°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm |