Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.04 g/cm³ Show Material materials with Dichte of 1.04 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.16 % Show Material materials with Wasserabsorption of 0.16 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.45 GPa Show Material materials with Biegemodul of 2.45 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 45 % Show Material materials with Dehnung of 45 % | ISO 527 | 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.4 GPa Show Material materials with Elastizitätsmodul of 2.4 GPa | ISO 527 | 1 mm/min |
Elongation at yield | 23.0 °C | 2.2 % Show Material materials with Elongation at yield of 2.2 % | ISO 527 | 50 mm/min |
Flexural yield strength | 23.0 °C | 65 MPa Show Material materials with Flexural yield strength of 65 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 129 [-] Show Material materials with Hardness, Rockwell R of 129 [-] | ISO 2039-2 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 23 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 23 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A |
23.0 °C | 18 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 18 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 45 MPa Show Material materials with Streckgrenze of 45 MPa | ISO 527 | 50 mm/min |
Zugfestigkeit | 23.0 °C | 35 MPa Show Material materials with Zugfestigkeit of 35 MPa | ISO 527 | 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75/Ae | 1.8 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8.7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8.7E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Vicat-Erweichungstemperatur | 100 °C Show Material materials with Vicat-Erweichungstemperatur of 100 °C | ISO 306 | Rate B/120 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.7E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.7E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 12 g/10min Show Material materials with Schmelzmassenflussrate of 12 g/10min | ISO 1133 | 220°C/5.0 kg | |
Schmelzvolumenflussrate | 39 cm³/10min Show Material materials with Schmelzvolumenflussrate of 39 cm³/10min | ISO 1133 | 220°C/10.0 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Enclosure/Housing/Cover | |
| Processing methods | Drying Temperature: 85-95°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 220-260°C, Nozzle Temperature: 210-250°C, Front - Zone 3 Temperature: 220-260°C, Middle - Zone 2 Temperature: 220-260°C, Rear - Zone 1 Temperature: 200-240°C, Hopper Temperature: 60-80°C, Mold Temperature: 40-80°C | |