Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.04 g/cm³ Show Material materials with Dichte of 1.04 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.2 GPa Show Material materials with Biegemodul of 2.2 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 20 % Show Material materials with Dehnung of 20 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.1 GPa Show Material materials with Elastizitätsmodul of 2.1 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 2.1 % Show Material materials with Elongation at yield of 2.1 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 68 MPa Show Material materials with Flexural yield strength of 68 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 293 J/m Show Material materials with Impact strength, Izod notched, ASTM of 293 J/m | ASTM D 256 |
Streckgrenze | 23.0 °C | 41 MPa Show Material materials with Streckgrenze of 41 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 31 MPa Show Material materials with Zugfestigkeit of 31 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 82 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 82 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8.64E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8.64E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 98 °C Show Material materials with Vicat-Erweichungstemperatur of 98 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.82E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.82E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating | 1.52mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 0 V Show Material materials with Kriechstromfestigkeit of 0 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 23.0 °C | 240 Pa·s Show Material materials with Melt viscosity of 240 Pa·s | ASTM D 3825 | 240°C, 1000 sec⁻¹ |
Schmelzmassenflussrate | 5.6 g/10min Show Material materials with Schmelzmassenflussrate of 5.6 g/10min | ASTM D 1238 | 230°C/3.8 kg | |
Schmelzvolumenflussrate | 18 cm³/10min Show Material materials with Schmelzvolumenflussrate of 18 cm³/10min | ISO 1133 | 220°C/10.0 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.8 % Show Material materials with Schrumpfung of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Heavy Vehicles,Lawn/Garden,Recreational Vehicle | |
| Processing methods | Drying Temperature: 80-95°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 220-260°C, Nozzle Temperature: 220-260°C, Front - Zone 3 Temperature: 215-240°C, Middle - Zone 2 Temperature: 205-225°C, Rear - Zone 1 Temperature: 190-210°C, Mold Temperature: 50-70°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm | |