Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.45 g/cm³ Show Material materials with Dichte of 1.45 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 2.41 GPa Show Material materials with Biegemodul of 2.41 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Elongation at yield | 23.0 °C | 30 % Show Material materials with Elongation at yield of 30 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 110 MPa Show Material materials with Flexural yield strength of 110 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 53 J/m Show Material materials with Impact strength, Izod notched, ASTM of 53 J/m | ASTM D 256 |
Streckgrenze | 23.0 °C | 68 MPa Show Material materials with Streckgrenze of 68 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 65 MPa Show Material materials with Zugfestigkeit of 65 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 154 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 154 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed |
Rheological Properties
Property | Value | Comment |
---|---|---|
Schmelzmassenflussrate | 6 g/10min Show Material materials with Schmelzmassenflussrate of 6 g/10min | ASTM D 1238 | 300°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Building/Construction Sheet | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 310-330°C, Nozzle Temperature: 305-325°C, Front - Zone 3 Temperature: 310-330°C, Middle - Zone 2 Temperature: 300-320°C, Rear - Zone 1 Temperature: 290-310°C, Mold Temperature: 80-115°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm |