Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.21 g/cm³ Show Material materials with Dichte of 1.21 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.15 % Show Material materials with Wasserabsorption of 0.15 % | ASTM D 570 | 24 Hours |
Wasseraufnahme, Gleichgewicht | 23.0 °C | 0.35 % Show Material materials with Wasseraufnahme, Gleichgewicht of 0.35 % | ASTM D 570 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.24 GPa Show Material materials with Biegemodul of 2.24 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 90 % Show Material materials with Dehnung of 90 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 91 MPa Show Material materials with Flexural yield strength of 91 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 |
Streckgrenze | 23.0 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 55 MPa Show Material materials with Zugfestigkeit of 55 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 132 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 132 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 151 °C Show Material materials with Vicat-Erweichungstemperatur of 151 °C | ASTM D 1525 | Rate B/50 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.19 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.19 W/(m·K) | ASTM C177 | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating | 1.11mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 2 V Show Material materials with Kriechstromfestigkeit of 2 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 10 g/10min Show Material materials with Schmelzmassenflussrate of 10 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Data Transfer,Electronic Components,Enclosure/Housing/Cover,Enclosures,Individual Equiptment,Security/Detection,Wireless Communications | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 295-315°C, Nozzle Temperature: 290-310°C, Front - Zone 3 Temperature: 295-315°C, Middle - Zone 2 Temperature: 280-305°C, Rear - Zone 1 Temperature: 270-295°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |