Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Material materials with Dichte of 1.19 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.2 % Show Material materials with Wasserabsorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 93 MPa Show Material materials with Biegefestigkeit of 93 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Biegemodul | 23.0 °C | 2.4 GPa Show Material materials with Biegemodul of 2.4 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 100 % Show Material materials with Dehnung of 100 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.42 GPa Show Material materials with Elastizitätsmodul of 2.42 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 550 J/m Show Material materials with Impact strength, Izod notched, ASTM of 550 J/m | ASTM D 256 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 11 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA | ||
23.0 °C | 40 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 40 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 11 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 11 kJ/m² | ISO 180/1A | ||
23.0 °C | 14 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 14 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 61 MPa Show Material materials with Streckgrenze of 61 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 51 MPa Show Material materials with Zugfestigkeit of 51 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 123 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 123 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8.1E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8.1E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 140 °C Show Material materials with Vicat-Erweichungstemperatur of 140 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.2E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 11 g/10min Show Material materials with Schmelzmassenflussrate of 11 g/10min | ASTM D 1238 | 250°C/1.2 kgf | |
Schmelzvolumenflussrate | 10 cm³/10min Show Material materials with Schmelzvolumenflussrate of 10 cm³/10min | ISO 1133 | 250°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.6 - 0.8 % Show Material materials with Schrumpfung of 0.6 - 0.8 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | -0.1 - 0 % Show Material materials with Schrumpfung, diagonal of -0.1 - 0 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Data Management | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 305-330°C, Nozzle Temperature: 305-330°C, Front - Zone 3 Temperature: 305-330°C, Middle - Zone 2 Temperature: 295-320°C, Rear - Zone 1 Temperature: 280-310°C, Mold Temperature: 65-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 60-200rpm | |