Allgemein
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.31 GPa Show Material materials with Biegemodul of 2.31 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Dehnung | 23.0 °C | 78 % Show Material materials with Dehnung of 78 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.3 GPa Show Material materials with Elastizitätsmodul of 2.3 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 97 MPa Show Material materials with Flexural yield strength of 97 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 128 J/m Show Material materials with Impact strength, Izod notched, ASTM of 128 J/m | ASTM D 256 | ||
23.0 °C | 910 J/m Show Material materials with Impact strength, Izod notched, ASTM of 910 J/m | ASTM D 256 | |||
Streckgrenze | 23.0 °C | 64 MPa Show Material materials with Streckgrenze of 64 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 60 MPa Show Material materials with Zugfestigkeit of 60 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ 23,-30°C | ASTM D 4812 | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 129 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.06E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.06E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 145 °C Show Material materials with Vicat-Erweichungstemperatur of 145 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.16E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.16E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.8 [-] Show Material materials with Dielektrizitätskonstante of 2.8 [-] | SABIC method | at 1.1 GHz |
Verlustfaktor | 23.0 °C | 6.3E-3 [-] Show Material materials with Verlustfaktor of 6.3E-3 [-] | SABIC method | at 1.1 GHz |
Optisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 8 cm³/10min Show Material materials with Schmelzvolumenflussrate of 8 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.77 % Show Material materials with Schrumpfung of 0.77 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.77 % Show Material materials with Schrumpfung, diagonal of 0.77 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Sunglasses | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-310°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-310°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-110°C | |