Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.36 g/cm³ Show Material materials with Dichte of 1.36 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.07 % Show Material materials with Wasserabsorption of 0.07 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 130 MPa Show Material materials with Biegefestigkeit of 130 MPa | ISO 178 |
Biegemodul | 23.0 °C | 4 GPa Show Material materials with Biegemodul of 4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 3.4 % Show Material materials with Dehnung of 3.4 % | ISO 527 | 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.55 GPa Show Material materials with Elastizitätsmodul of 4.55 GPa | ISO 527 | 1 mm/min |
Elongation at yield | 23.0 °C | 3.4 % Show Material materials with Elongation at yield of 3.4 % | ISO 527 | 5 mm/min |
Flexural strain | 23.0 °C | 5 % Show Material materials with Flexural strain of 5 % | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 130 MPa Show Material materials with Flexural yield strength of 130 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 110 MPa Show Material materials with Hardness, Ball Indentation of 110 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 30 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 30 kJ/m² | ISO 179/1eU |
23.0 °C | 30 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 30 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 4 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A |
23.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 25 kJ/m² | ISO 180/1U |
23.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 25 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 90 MPa Show Material materials with Streckgrenze of 90 MPa | ISO 527 | 5 mm/min |
Zugfestigkeit | 23.0 °C | 90 MPa Show Material materials with Zugfestigkeit of 90 MPa | ISO 527 | 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 215 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75/Bf | 0.45 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 220 °C Show Material materials with Vicat-Erweichungstemperatur of 220 °C | ASTM D 1525 | Rate A/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94HB Flame Class Rating | 1.6mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.4 [-] Show Material materials with Dielektrizitätskonstante of 3.4 [-] | ASTM D 150 | at 1 MHz |
Durchschlagfestigkeit | 23.0 °C | 18 kV/mm Show Material materials with Durchschlagfestigkeit of 18 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Kriechstromfestigkeit | 23.0 °C | 325 V Show Material materials with Kriechstromfestigkeit of 325 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 0.02 [-] Show Material materials with Verlustfaktor of 0.02 [-] | ASTM D 150 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 260.0 °C | 100 Pa·s Show Material materials with Melt viscosity of 100 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzvolumenflussrate | 28 cm³/10min Show Material materials with Schmelzvolumenflussrate of 28 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.9 % Show Material materials with Schrumpfung of 0.5 - 0.9 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.7 - 1.1 % Show Material materials with Schrumpfung, diagonal of 0.7 - 1.1 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive connectors. | |
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |