Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.39 g/cm³ Show Material materials with Dichte of 1.39 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 120 MPa Show Material materials with Biegefestigkeit of 120 MPa | ISO 178 |
Biegemodul | 23.0 °C | 4.8 GPa Show Material materials with Biegemodul of 4.8 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 3 % Show Material materials with Dehnung of 3 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 5.3 GPa Show Material materials with Elastizitätsmodul of 5.3 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural strain | 23.0 °C | 3 % Show Material materials with Flexural strain of 3 % | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 120 MPa Show Material materials with Flexural yield strength of 120 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 160 MPa Show Material materials with Hardness, Ball Indentation of 160 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/2C |
23.0 °C | 4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/2C | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | ISO 179/2C |
23.0 °C | 30 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 30 kJ/m² | ISO 179/2C | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 4 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A |
23.0 °C | 4 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 20 kJ/m² | ISO 180/1U |
23.0 °C | 28 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 28 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 85 MPa Show Material materials with Streckgrenze of 85 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 85 MPa Show Material materials with Zugfestigkeit of 85 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 260.0 °C | 90 Pa·s Show Material materials with Melt viscosity of 90 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzvolumenflussrate | 40 cm³/10min Show Material materials with Schmelzvolumenflussrate of 40 cm³/10min | ISO 1133 | 250°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.2 - 0.6 % Show Material materials with Schrumpfung of 0.2 - 0.6 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive | |
| Fillers | 15% Glass Fiber | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |