Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.32 g/cm³ Show Material materials with Dichte of 1.32 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.08 % Show Material materials with Wasserabsorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.5 GPa Show Material materials with Biegemodul of 2.5 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 100 % Show Material materials with Dehnung of 100 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.8 GPa Show Material materials with Elastizitätsmodul of 2.8 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 20 % Show Material materials with Elongation at yield of 20 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 46 J/m Show Material materials with Impact strength, Izod notched, ASTM of 46 J/m | ASTM D 256 | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/1eA | ||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 2 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 2 kJ/m² | ISO 180/1A | ||
23.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 59 MPa Show Material materials with Streckgrenze of 59 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ -30°C | ASTM D 4812 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 54 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 54 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8.4E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 185 °C Show Material materials with Vicat-Erweichungstemperatur of 185 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating | 1.5mm | UL 94 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 35.4 g/10min Show Material materials with Schmelzmassenflussrate of 35.4 g/10min | ASTM D 1238 | 250°C/2.16 kg | |
Schmelzvolumenflussrate | 34 cm³/10min Show Material materials with Schmelzvolumenflussrate of 34 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Schrumpfung | 23.0 °C | 2.1 - 2.4 % Show Material materials with Schrumpfung of 2.1 - 2.4 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Dishwasher,Forward Lighting,Meter Gas,Non-LED Lighting,Rear/Signal Lighting,Trim | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 245-260°C, Nozzle Temperature: 240-255°C, Front - Zone 3 Temperature: 245-260°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-250°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.025mm |