Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.64 g/cm³ Show Material materials with Dichte of 1.64 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.06 % Show Material materials with Wasserabsorption of 0.06 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 182 MPa Show Material materials with Biegefestigkeit of 182 MPa | ISO 178 |
Biegemodul | 23.0 °C | 7.87 GPa Show Material materials with Biegemodul of 7.87 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2.3 % Show Material materials with Dehnung of 2.3 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 9.75 GPa Show Material materials with Elastizitätsmodul of 9.75 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 2.2 % Show Material materials with Elongation at yield of 2.2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural strain | 23.0 °C | 2.9 % Show Material materials with Flexural strain of 2.9 % | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 183 MPa Show Material materials with Flexural yield strength of 183 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 74 J/m Show Material materials with Impact strength, Izod notched, ASTM of 74 J/m | ASTM D 256 |
23.0 °C | 90 J/m Show Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 116 MPa Show Material materials with Streckgrenze of 116 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 114 MPa Show Material materials with Zugfestigkeit of 114 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 205 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.35E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.35E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Vicat-Erweichungstemperatur | 176 °C Show Material materials with Vicat-Erweichungstemperatur of 176 °C | ASTM D 1525 | Rate B/50 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.14E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.14E-4 1/K | ASTM E 831 | -40°C to 95°C | ||
Entflammbarkeit | UL Compliant, 94V-0 Flame Class Rating | 0.8mm | UL 94 by SABIC-IP | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 17.8 g/10min Show Material materials with Schmelzmassenflussrate of 17.8 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Schmelzvolumenflussrate | 12 cm³/10min Show Material materials with Schmelzvolumenflussrate of 12 cm³/10min | ISO 1133 | 250°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.18 - 0.21 % Show Material materials with Schrumpfung of 0.18 - 0.21 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.75 - 0.94 % Show Material materials with Schrumpfung, diagonal of 0.75 - 0.94 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Building Element,Electronic Components,Enclosures,Lawn/Garden,Non-LED Lighting,Photo/Video Camera,Photovoltaic Components,Power Manangement | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 230-260°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 240-260°C, Middle - Zone 2 Temperature: 230-250°C, Rear - Zone 1 Temperature: 220-240°C, Mold Temperature: 60-120°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 20-100rpm, Shot to Cylinder Size: 30-70%, Vent Depth: 0.025-0.038mm | |