Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.31 g/cm³ Show Material materials with Dichte of 1.31 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.08 % Show Material materials with Wasserabsorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.6 GPa Show Material materials with Biegemodul of 2.6 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 15 % Show Material materials with Dehnung of 15 % | ISO 527 | 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.8 GPa Show Material materials with Elastizitätsmodul of 2.8 GPa | ISO 527 | 1 mm/min | ||
Elongation at yield | 23.0 °C | 3.5 % Show Material materials with Elongation at yield of 3.5 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 85 MPa Show Material materials with Flexural yield strength of 85 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 100 MPa Show Material materials with Hardness, Ball Indentation of 100 MPa | ISO 2039-1 | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 3 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | ISO 179/1eA | ||
23.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 2 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 2 kJ/m² | ISO 180/1A | ||
23.0 °C | 2 - 4 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 2 - 4 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 65 MPa Show Material materials with Streckgrenze of 65 MPa | ISO 527 | 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 50 MPa Show Material materials with Zugfestigkeit of 50 MPa | ISO 527 | 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No break @ 23,-30°C | ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75/Ae | 1.8 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.3E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Vicat-Erweichungstemperatur | 185 °C Show Material materials with Vicat-Erweichungstemperatur of 185 °C | ISO 306 | Rate B/120 | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.3E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Entflammbarkeit | UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.1 [-] Show Material materials with Dielektrizitätskonstante of 3.1 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 16 kV/mm Show Material materials with Durchschlagfestigkeit of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 0.02 [-] Show Material materials with Verlustfaktor of 0.02 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 20 cm³/10min Show Material materials with Schmelzvolumenflussrate of 20 cm³/10min | ISO 1133 | 250°C/1.2 kg | |
Schrumpfung | 23.0 °C | 1.1 - 1.8 % Show Material materials with Schrumpfung of 1.1 - 1.8 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.9 - 1.8 % Show Material materials with Schrumpfung, diagonal of 0.9 - 1.8 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components,Wiring Devices | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |