Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.3 g/cm³ Show Material materials with Dichte of 1.3 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 115 MPa Show Material materials with Biegefestigkeit of 115 MPa | ISO 178 |
Biegemodul | 23.0 °C | 3.8 GPa Show Material materials with Biegemodul of 3.8 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 3 % Show Material materials with Dehnung of 3 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.6 GPa Show Material materials with Elastizitätsmodul of 4.6 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural strain | 23.0 °C | 4 % Show Material materials with Flexural strain of 4 % | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 120 MPa Show Material materials with Flexural yield strength of 120 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 100 MPa Show Material materials with Hardness, Ball Indentation of 100 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Impact strength, Izod notched, ASTM | -30.0 °C | 45 J/m Show Material materials with Impact strength, Izod notched, ASTM of 45 J/m | ASTM D 256 |
23.0 °C | 55 J/m Show Material materials with Impact strength, Izod notched, ASTM of 55 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 340 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 340 J/m | ASTM D 4812 |
23.0 °C | 440 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 440 J/m | ASTM D 4812 | |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/2C |
23.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/2C | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | ISO 179/2C |
23.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 45 kJ/m² | ISO 179/2C | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A |
23.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 25 kJ/m² | ISO 180/1U |
23.0 °C | 30 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 30 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 80 MPa Show Material materials with Streckgrenze of 80 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 80 MPa Show Material materials with Zugfestigkeit of 80 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 205 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 205 °C | ISO 75/Bf | 0.45 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3.57E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 3.57E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Vicat-Erweichungstemperatur | 150 °C Show Material materials with Vicat-Erweichungstemperatur of 150 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.96E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.96E-4 1/K | ISO 11359-2 | 23°C to 150°C |
Elektrisch
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 260.0 °C | 160 Pa·s Show Material materials with Melt viscosity of 160 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzmassenflussrate | 40 g/10min Show Material materials with Schmelzmassenflussrate of 40 g/10min | ASTM D 1238 | 265°C/5.0 kgf | |
Schmelzvolumenflussrate | 35 cm³/10min Show Material materials with Schmelzvolumenflussrate of 35 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.6 - 0.8 % Show Material materials with Schrumpfung of 0.6 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components,Monitoring and Imaging | |
Fillers | 10% Glass Fiber | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C |