Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.38 g/cm³ Show Material materials with Dichte of 1.38 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.27 % Show Material materials with Wasserabsorption of 0.27 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 155 MPa Show Material materials with Biegefestigkeit of 155 MPa | ISO 178 |
Biegemodul | 23.0 °C | 5.7 GPa Show Material materials with Biegemodul of 5.7 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 3 % Show Material materials with Dehnung of 3 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 7.2 GPa Show Material materials with Elastizitätsmodul of 7.2 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural strain | 23.0 °C | 4 % Show Material materials with Flexural strain of 4 % | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 155 MPa Show Material materials with Flexural yield strength of 155 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 130 MPa Show Material materials with Hardness, Ball Indentation of 130 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ISO 2039-2 |
Impact strength, Izod notched, ASTM | -30.0 °C | 70 J/m Show Material materials with Impact strength, Izod notched, ASTM of 70 J/m | ASTM D 256 |
23.0 °C | 80 J/m Show Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 605 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 605 J/m | ASTM D 4812 |
23.0 °C | 680 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 680 J/m | ASTM D 4812 | |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/2C |
23.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/2C | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 40 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 45 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A |
23.0 °C | 7 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 40 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 40 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 45 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 105 MPa Show Material materials with Streckgrenze of 105 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 105 MPa Show Material materials with Zugfestigkeit of 105 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 170 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 170 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 3E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 170 °C Show Material materials with Vicat-Erweichungstemperatur of 170 °C | ASTM D 1525 | Rate B/50 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.25 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.25 W/(m·K) | ISO 8302 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.05E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.05E-4 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Compliant, 94HB Flame Class Rating | 1.6mm | UL 94 by SABIC-IP | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.4 [-] Show Material materials with Dielektrizitätskonstante of 3.4 [-] | ASTM D 150 | at 1 MHz |
Durchschlagfestigkeit | 23.0 °C | 24 kV/mm Show Material materials with Durchschlagfestigkeit of 24 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Kriechstromfestigkeit | 23.0 °C | 1 V Show Material materials with Kriechstromfestigkeit of 1 V | UL 746A |
Verlustfaktor | 23.0 °C | 0.02 [-] Show Material materials with Verlustfaktor of 0.02 [-] | ASTM D 150 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 260.0 °C | 175 Pa·s Show Material materials with Melt viscosity of 175 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzmassenflussrate | 35 g/10min Show Material materials with Schmelzmassenflussrate of 35 g/10min | ASTM D 1238 | 265°C/5.0 kgf | |
Schmelzvolumenflussrate | 30 cm³/10min Show Material materials with Schmelzvolumenflussrate of 30 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.3 - 0.6 % Show Material materials with Schrumpfung of 0.3 - 0.6 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.4 - 0.8 % Show Material materials with Schrumpfung, diagonal of 0.4 - 0.8 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Electronic Components,Enclosures,Exterior Trim,Forward Lighting,Gas/Electric Oven,Meter Gas,Wiring Devices | |
| Fillers | 20% Glass Fiber | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |