Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.64 GPa Show Material materials with Biegemodul of 2.64 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 100 MPa Show Material materials with Flexural yield strength of 100 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -20.0 °C | 127 J/m Show Material materials with Impact strength, Izod notched, ASTM of 127 J/m | ASTM D 256 |
23.0 °C | 209 J/m Show Material materials with Impact strength, Izod notched, ASTM of 209 J/m | ASTM D 256 | |
Thermisch
| Property | Value | Comment |
|---|---|---|
Heat deflection temperature, 1.80 MPa | 90 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Schmelzvolumenflussrate | 35 cm³/10min Show Material materials with Schmelzvolumenflussrate of 35 cm³/10min | ISO 1133 | 265°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Personal Care | |
| Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-280°C, Nozzle Temperature: 255-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 255-275°C, Rear - Zone 1 Temperature: 250-270°C, Mold Temperature: 65-95°C, Back Pressure: 0.3-0.6MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm | |